CA Series-770CA30 PEEK Carbon Fiber Reinforcement

CA Series-770CA30 PEEK carbon fiber reinforcement is widely used in automobile and aviation fields. It is widely used in automobile fuel pump and gearbox. It can help equipment reduce weight, reduce noise and increase the service life of wear-resistant parts, reduce or even avoid the use of lubricants.

Contact ZYPEEK

Specification of CA Series-770CA30 PEEK Carbon Fiber Reinforcement


Material PropertiesTest MethodConditionsUnits770G
Mechanical Data
Tensile StrengthISO 527B reak,23℃MPa-
Y ield,23℃MPa100
Tensile ElogationISO 527Break,23℃%45
Flexural StrengthISO 178Break,23℃MPa-
Y ield,23℃MPa165
Fleoural ModulusISO 17823℃Gpa4.1
Compressive StrengthISO 60423℃MPa125
Charpy Impact StrengthISO 179/leANotchedkJm-27
ISO 179/IUUnnotchedkJm-2-
Izod Impact StrengthISO 180/ANotchedkJm-27.5
ISO 180/UUnnotchedkJm-2-
Mould ShrinkageISO 294-4Along flow%1
Across flow%1.3
Thermal Data
Melting PointISO 11357
343
Glass Tansition (Tg)ISO 11357Onset143
Special Heat CapacityDSC23℃kj kg-1℃-12.2
Coefficient of Thermal ExpansionISO 11359Along flow below Tgppm K-145
Along flow above Tgppm K-1120
Heat Deflecion TemperatureISO 75A-f1.8Mpa152
Thermal ConductivityASTM C17723℃W m-1K-10.29
Flow
MeltIndexISO 1133380℃,5kgg10min-110
Miscellaneous
DensityISO 1186Crystallinegcm-31.3
Amorphousgcm-31.26
Shore D HardnessISO 86823℃
85
Water Absorption(3.2mm thick Tensile Bar)ISO 62-124h,23℃%0.07
by immersion
Equilib riu m,23℃%0.4
Electrical Data
Dielectric StrengthIEC 60243-12mmkV mm-123
Comparative Tracking IndexIEC 60112
V150
Dielectric ConstantIEC 6025023℃,1kHz
3.1
23℃,50kHz
3
Loss TangentIEC 6025023℃,1MHz
0.004
Volume ResistivityIEC 6009323℃,1VΩ cm10 16
275℃Ω cm10 9


Products
Finding Professional PEEK Raw Material Supplier? Get In Touch With ZYPEEK!

Other Grade CA Carbon Fiber Reinforcement PEEK

Latest PEEK News & Blog
We use cookies to offer you a better browsing experience, analyze site traffic and personalize content. By using this site, you agree to our use of cookies. Visit our cookie policy to learn more.
Reject Accept